Title: Fatigue of stress corrosion cracks in X65 pipeline steels
Author: Gamboa, E.
Linton, V.
Law, M.
Citation: International Journal of Fatigue, 2008; 30(5):850-860
Publisher: Elsevier Sci Ltd
Issue Date: 2008
ISSN: 0142-1123
Statement of
Responsibility: 
E. Gamboa, V. Linton and M. Law
Abstract: A section of gas pipeline containing stress corrosion cracking (SCC) was removed from service and pressure cycled. SCC cracks were shown to have extended by fatigue. Fatigue crack interaction was found to be a large factor in crack growth characteristics. Crack interaction was found to be influenced by original SCC crack inclination and layout. Fatigue crack growth was found to be independent of original SCC crack profile or aspect ratio.
Keywords: SCC; Pipeline fatigue; Crack interaction
RMID: 0020080459
DOI: 10.1016/j.ijfatigue.2007.06.006
Description (link): http://www.elsevier.com/wps/find/journaldescription.cws_home/30433/description#description
Appears in Collections:Mechanical Engineering publications
Materials Research Group publications

Files in This Item:
There are no files associated with this item.


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.